Detailed Properties and Specifications for Alloy 464
Source: Copper Development Association
Composition
| Cu 59.0-62.0 |
Pb 0.20max |
Fe 0.10max |
Sn 0.50-1.0 |
Zn Rem |
Fabrication Properties
| Property |
|
Rating |
| Capacity for being cold worked |
|
Fair |
| Capacity for being hot formed |
|
Excellent |
| Hot forge-ability rating (Forging brass=100) |
|
90 |
| Hot working temperature |
|
1200-1500F |
| Annealing temperature |
|
800-1000F |
| Machine-ability rating (Free cutting brass=100) |
|
30 |
| Soldering |
|
Excellent |
| Brazing |
|
Excellent |
| Oxyacetylene welding |
|
Good |
| Gas shielding arc welding |
|
Fair |
| Coated metal arc welding |
|
Not Recommended |
| Resistance welding (Spot) |
|
Good |
| Resistance welding (Seam) |
|
Fair |
| Resistance welding (Butt) |
|
Good |
Specific Properties based on ASTM B171
| Diameter |
Temper |
Tensile Strength |
Elongation |
Yield Strength |
Rockwell Hardness |
|
3" & under |
Soft (M20) |
50min |
35min |
20min |
|
|
>3" |
Soft (M20) |
50min |
35min |
18min |
|
|
1/2" & under |
Half-Hard |
60min |
22min |
27min |
|
|
>1/2" to 1" |
Half-Hard |
60min |
25min |
27min |
|
|
>1" to 2" |
Half-Hard |
58min |
25min |
26min |
|
|
>2" to 3" |
Half-Hard |
54min |
25min |
25min |
|
|
>3" to 4" |
Half-Hard |
54min |
27min |
22min |
|
| Over 4" OD |
Half-Hard |
54min |
30min |
22min |
|
Other Alloys:
110,
220,
260,
280,
330,
360,
464,
510,
614,
706,
715,
932,
936,
& 954