Detailed Properties and Specifications for Alloy 360
Source: Copper Development Association
Composition
| Cu 60.0-63.0 |
Pb 2.5-3.7 |
Fe 0.35max |
Zn Rem |
Fabrication Properties
| Property |
|
Rating |
| Capacity for being cold worked |
|
Poor |
| Capacity for being hot formed |
|
Fair |
| Hot forge-ability rating (Forging brass=100) |
|
|
| Hot working temperature |
|
1300-1450F |
| Annealing temperature |
|
800-1100F |
| Machine-ability rating (Free cutting brass=100) |
|
100 |
| Soldering |
|
Excellent |
| Brazing |
|
Good |
| Oxyacetylene welding |
|
Not Recommended |
| Gas shielding arc welding |
|
Not Recommended |
| Coated metal arc welding |
|
Not Recommended |
| Resistance welding (Spot) |
|
Not Recommended |
| Resistance welding (Seam) |
|
Not Recommended |
| Resistance welding (Butt) |
|
Fair |
Specific Properties based on ASTM B16
| Diameter |
Temper |
Tensile Strength |
Elongation |
Yield Strength |
Rockwell Hardness |
|
1/2" & under |
Half-Hard |
57min |
7min |
25min |
|
|
>1/2" to 1" |
Half-Hard |
55min |
10min |
25min |
|
|
>1" to 2" |
Half-Hard |
50min |
15min |
20min |
|
|
>2" to 4" |
Half-Hard |
45min |
20min |
15min |
|
|
Over 4" OD |
Half-Hard |
40min |
20min |
15min |
|
|
1/2" & under |
Half-Hard |
50min |
10min |
25min |
|
|
1/2" & under |
Half-Hard |
45min |
15min |
17min |
|
|
>1/2" to 2" |
Half-Hard |
45min |
15min |
17min |
|
|
>1/2" to 2" |
Half-Hard |
40min |
20min |
15min |
|
|
>2" to 3" |
Half-Hard |
40min |
20min |
15min |
|