Detailed Properties and Specifications for Alloy 110
Source: Copper Development Association
Composition
Cu 99.90
Fabrication Properties
| Property |
|
Rating |
| Capacity for being cold worked |
|
Excellent |
| Capacity for being hot formed |
|
Excellent |
| Hot forge-ability rating (Forging brass=100) |
|
65 |
| Hot working temperature |
|
1400-1600F |
| Annealing temperature |
|
700-1200F |
| Machine-ability rating (Free cutting brass=100) |
|
20 |
| Soldering |
|
Excellent |
| Brazing |
|
Good |
| Oxyacetylene welding |
|
Not Recommended |
| Gas shielding arc welding |
|
Fair |
| Coated metal arc welding |
|
Not Recommended |
| Resistance welding (Spot) |
|
Not Recommended |
| Resistance welding (Seam) |
|
Not Recommended |
| Resistance welding (Butt) |
|
Good |
Specific Properties based on ASTM B187
| Diameter |
Temper |
Tensile Strength |
Elongation |
Yield Strength |
Rockwell Hardness |
| Up to 3/8" |
Hard |
45min-55max |
|
|
|
| >3/8" to 1" |
Hard |
40min-50max |
|
|
80min |
| >1" to 2" |
Hard |
35min-45max |
|
|
75min |
| >2" to 3" |
Hard |
44min-43max |
|
|
65min |
| 3/8" thk to 4" wide |
Hard |
37.5min-50max |
10min |
|
80min |
| All sizes |
CR 1/8Hard |
32min-40max |
|
|
54-82 |
| All Sizes |
CR 1/4 Hard |
34min-42max |
|
|
60-84 |
| All sizes |
CR 1/2Hard |
37min-46max |
|
|
77-89 |
Other Alloys:
110,
220,
260,
280,
330,
360,
464,
510,
614,
706,
715,
932,
936,
& 954